| 镀液维护 |
| 添加时间：2019/10/11 15:07:26 浏览次数： |
| 1、柔软剂及光亮剂以1：1添加为宜，光亮剂消耗量为0.4ml/LKA·H，柔软剂消耗量为0.4ml/LKA·H，柔软剂提高走位作用廉低区深镀作用，亮度不足时可添加光亮剂，用清水或电镀溶液稀释后加入浴槽中。 1. Softener and brightener should be added at 1:1. The consumption of brightener is 0.4ml/LKA.H, the consumption of softener is 0.4ml/LKA.H. Softener can improve the deep plating effect in low-cost areas. When the brightness is insufficient, brightener can be added. After dilution with water or electroplating solution, brightener can be added to bath. 2、正常生产中，只须添加柔软剂光亮剂，氯化钾和硼酸，滚镀锌含量可通过分析补加，吊镀氯化锌一般在5-7天加一次（通电160小时以上），每升添加3-5克为宜。 2. In normal production, only softener brightener, potassium chloride and boric acid are needed. The content of barrel galvanizing can be supplemented by analysis. The suspension galvanizing is usually added once every 5-7 days (more than 160 hours of electrification). It is advisable to add 3-5 grams per liter. 3、在生产中，氢离子会逐渐升高，可用盐酸调整PH值至规定的范围。 3. Hydrogen ions will gradually increase in production. Hydrochloric acid can be used to adjust the PH value to the prescribed range. 4、电镀浴液4个月一小处理，6个月一大处理，以保证镀锌层质量。 4. Electroplating bath is treated in a small amount for 4 months and in a large amount for 6 months to ensure the quality of galvanized layer. 5、滚镀通电96小时需加高锰酸钾每方镀液按0.3公斤用热水溶解加入镀液里除去镀液里产生的铁杂质。 5. For 96 hours of barrel plating, potassium permanganate should be added to each plating solution and dissolved in hot water at 0.3 kg to remove iron impurities from the plating solution. 6、吊镀通电160小时需加高锰酸钾每方镀液按0.3公斤用热水溶解加入镀液里，除去镀液里产生的铁杂质。 6. Potassium permanganate should be added to the plating solution for 160 hours, and 0.3 kg hot water should be dissolved into the plating solution to remove the iron impurities produced in the plating solution. |
| 上一页 塑料光亮剂具有润滑性 |
| 下一页 镍次级光亮剂一般由以下几个部分组成 |
Copyright © 技术支持：遨游网络